Non-ferrous Metals
Metal Capillary
Advanced Ceramics
Boron Nitride Ceramic
Pyrolytic Boron Nitride
Silicon Nitride Ceramic
Aluminum Nitride Ceramic
Zirconia Ceramic
Alumina Ceramic
Silicon Carbide Ceramic
Deposition Materials
Semimetal Elements
Functional Materials
Neodymium Magnets
Neodymium Disc Magnets
Neodymium Cylinder Magnets
Neodymium Block Magnets
Neodymium Ring Magnets
Neodymium Countersunk Magnets
Magnetic Assemblies
Arc Magnets
Custom Shaped Magnets
Rare Earth Elements
Metal and Alloy Powder
We provide pure metal powder and alloy powder for thermal spray coatings.
| Product | Material | Particle size | Application | Inquiry |
| Aluminum Powder | Al, 99-99.95% |
-90 +45 µm -75 +45 µm |
-Good electrical and thermal conductivity; non- magnetic, can be used for RF shielding -Corrosion resistant in coastal and industrial at- mospheric conditions -Relatively soft and ductile -Use to repair aluminum and magnesium alloy parts |
Inquiry |
| Copper Powder |
Cu, 99-99.95% |
-75 +31 µm -90 +38 µm |
-Excellent electrical and thermal conductivity; non-magnetic and usable for EMI shielding -Resistant to corrosive inks -Use to repair copper-base alloy parts |
Inquiry |
| Molybdenum Powder |
Mo, ≥99% |
-75 +38 µm -75 +30 µm -45 +16 µm |
-Tough and hard with excellent sliding proper- ties and good running properties -Resists fretting and electric arc erosion Service up to 320 °C (610 °F) |
Inquiry |
| Tungsten Powder |
W, ≥99.9% |
-75 +30 µm -45 +16 µm |
-High temperature situation -W-Re thermocouple -contact alloy etc |
Inquiry |
| Tin Powder |
Sn, 99.5% |
100mesh, -200mesh -325mesh |
-Additive and cellular material | Inquiry |
| Silicon Powder |
Si, 99.9~99.999% |
100-325mesh 10-100um |
-Widely used in electronics, diamond tools and other industries. | Inquiry |
| Nickel Powder | Ni, >99.3% |
-150 +45 µm -75 +45 µm |
-For salvage and build-up of nickel-based components to repair damage or mis-machining -Can replace Monel for corrosion applications when slightly higher hardness and machinability is needed |
Inquiry |
| Titanium Powder |
Ti, 99.5% |
-250 +90 µm -180 +53 µm -90 +18 µm -75 µm |
-Biocompatibility for medical applications -Can produce coatings with porous structures for implants -Corrosion resistant -Bond coat for hydroxyapatite top coats Service up to 425 °C (797 °F) |
Inquiry |
| Silver Powder | Ag, 99% | -120+325mesh | Working temp. <340℃, Corrosion resistance to acid, alkali and salt. Spray coating for aviation parts | Inquiry |
| Stainless Steel Powder |
304L, 316L, 317L 410L, 430L, 434L |
+100mesh, -325mesh |
Precision machinery parts | Inquiry |
| Nickel Chromium Alloy Powder | Ni50Cr | -140+325mesh | High chromium nickel alloy is wear and corrosion resistance, HRC-25, Working temp. <900℃, similar usage with Ni20Cr. Coating by plasma spray & HVOF, used as basic layer for ceramic coating or used as corrosion resistance coating. | Inquiry |
| Nickel Chromium Alloy Powder | Ni20Cr |
-140+325mesh -45+15 µm |
HRC-20, Working temp. <900℃, excellent corrosion resistance. Coating by plasma spray & HVOF, used as basic layer for ceramic coating or used as corrosion resistance coating. | Inquiry |
| Nickel Based Alloy Powder |
Ni6Co6Cr1Ti- 3Mo4Al30W3Fe |
-140+325mesh | HRC-32 (800℃), HRC-16 (900℃),, Great high temperature red-hardness, Impact resistance, wear & high temp resistance. Used for large seamless steel pipe ends, continuous caster blade, used to protect the surface of hot rolling machine | Inquiry |
| Nickel Based Alloy Powder | Ni5Cr1B2Si5Fe | -140+325mesh | Self-fluxing alloy powder, HRC-15, Working temp. <700℃, low hardness, good ductility, used for oxygen acetylene spray welding & laser cladding, spay welding for glass mold and casting parts repairing. | Inquiry |
| Nickel Based Alloy Powder | Ni7Cr1.5B2.8Si5Fe | -140+325mesh | Self-fluxing alloy powder, HRC-20/30, Working temp. <700℃, low hardness, good ductility, used for oxygen acetylene spray welding & laser cladding, spay welding for glass mold, bearing, surface corrosion resistance coating and casting parts repairing. | Inquiry |
| Nickel Based Alloy Powder | Ni9Cr2B3Si5Fe | -140+325mesh | Self-fluxing alloy powder, HRC-30/40, Working temp. <650℃, low hardness, good ductility, resistance to intermetallic friction. used for oxygen acetylene spray welding & laser cladding, spay welding for glass mold, bearing, plunger and surface corrosion resistance coating for bearing. | Inquiry |
| Nickel Based Alloy Powder | Ni3Cr2.5B3Si10Fe | -140+325mesh | Self-fluxing alloy powder, HRC-40/50, Working temp. <650℃, low hardness, good ductility, resistance to intermetallic friction. used for oxygen acetylene spray welding & laser cladding, spay welding for bearing, plunger, exhaust valve and valve seat. Surface corrosion resistance coating for bearing. | Inquiry |
| Nickel Based Alloy Powder | Ni15Cr3B3Si10Fe | -140+325mesh | Self-fluxing alloy powder, HRC-53/58, Working temp. <650℃, good hardness, Low coefficient of friction, resistance to intermetallic friction. used for oxygen acetylene spray welding, Induction remelting & laser cladding, Repairing or protecting hard surface wearing parts such as oil-well pump plunger and axile. | Inquiry |
| Nickel Based Alloy Powder | Ni17Cr3.5B4Si3Fe |
-140+325mesh -45+15 µm |
Self-fluxing alloy powder, HRC-58/62, Working temp. <650℃, High hardness, Low coefficient of friction, Wear & corrosion resistance, resistance to intermetallic friction. used for oxygen acetylene spray welding, Induction remelting & laser cladding, Repairing or protecting hard surface wearing parts such as oil-well pump plunger, conveyor roller, drawing tower wheel, extruder screw, etc. | Inquiry |
| Nickel Based Alloy Powder | Ni17Cr3.5B4Si2Fe |
-140+325mesh -45+15 µm |
Self-fluxing alloy powder, HRC-58/62, Working temp. <650℃, Spay coating for low corrosion resistance work pieces | Inquiry |
| Nickel Based Alloy Powder | Ni17Cr3.5B4Si10Fe | -140+325mesh | Self-fluxing alloy powder, HRC-40/50, Working temp. <650℃, low hardness, good ductility, resistance to intermetallic friction. used for oxygen acetylene spray welding & laser cladding, spay welding for bearing, plunger, exhaust valve and valve seat. Surface corrosion resistance coating for bearing. | Inquiry |
| Nickel Based Alloy Powder | Ni60+35WC-Ni | -140+325mesh | Self-fluxing alloy powder, HRC-60/75, Working temp. <650℃, Good wear resistance, Good self-fluxing, abrasive wear resistance is excellent. Spay welding for Drawing machine tower wheel, fan blades, system to the machine Sucrose pressure, mud pump plunger, etc. | Inquiry |
| Nickel Based Alloy Powder | Ni60+50WC-Co |
-140+325mesh -45+15 µm |
Self-fluxing alloy powder, HRC-60/75, Working temp. <600℃, Good wear resistance. Work pieces for brick making machines, sediment mixing, extruder screws, and wear parts for agricultural equipment | Inquiry |
| Nickel Based Alloy Powder | Ni60+30WC-Co | -140+325mesh | Self-fluxing alloy powder, HRC-60/72, Working temp. <600℃. Applied to spay welding for wire-drawing cone. | Inquiry |
| Nickel Aluminum Tungsten Alloy Powder | Ni22Al11.5W | -325mesh | HRC-30, Working temp. <850℃, Used as bonding layer of aircraft engines seal coating | Inquiry |
| Haynes Alloy Powder |
Ni21Cr3W- 15Mo2Fe2Co |
-140+325mesh | HRC-20, Working temp. <900℃, Haynes alloy C22, great corrosion resistance, and good wear resistance | Inquiry |
| Aluminum Bronze Alloy Powder | Cu10Al | -140+325mesh | HRC<20, Working temp. <400℃, Repairing copper & copper alloy parts, support surface coating for shafts | Inquiry |
| Copper Nickel Indium Alloy Powder | Cu35Ni5In | -140+325mesh | HRC<20, Working temp. <400℃, Coating with great compactness, wear-resistant and cavitation, good machinery performance, better anti-scratch and lubrication characteristics than copper-nickel alloy, plasma spraying, flame spraying, expansion joints, air compressor seals, aviation components | Inquiry |
| Cobalt Chromium Molybdenum Silicon Alloy Powder | Co8Cr28Mo2.6Si | -140+325mesh | HRC~35, Working temp. <840℃, Great resistance to corrosion & high temperature, plasma and HVOF spraying for aviation components | Inquiry |
| Cobalt Chromium Tungsten Alloy Powder |
Co31.5Cr12.5W- 2.5C3NiC1.4Si |
-140+325mesh | HRC~48/55, Working temp. <840℃, Great resistance to corrosion & high temperature, Impact resistance, anti-adhesion wear performance. Plasma surfacing for valve seats, bearings, blade, etc. | Inquiry |
| Cobalt Chromium Tungsten Alloy Powder |
Co30Cr4.5W1C- 3NiC1.4Si |
-60+160mesh |
HRC~40/55, Working temp. <840℃, Great resistance to high temperature corrosion, Plasma surfacing for HPHT valve, engine valve, blade, etc. | Inquiry |
| Cobalt Chromium Tungsten Alloy Powder |
Co28Cr5W0.25C- 3Ni1Si |
-140+325mesh | HRC~30, Working temp. <840℃, Great resistance to high temperature corrosion, Plasma surfacing for HPHT valve, engine valve, blade, etc. | Inquiry |
| Cobalt Chromium Tungsten Alloy Powder |
Co25.5Cr7.5W- 0.5C10.5Ni1Si |
-140+325mesh | HRC~48/55, Working temp. <840℃, Great resistance to corrosion & high temperature. Plasma surfacing for extrusion die, gas turbine blade, etc. | Inquiry |
| Cobalt Chromium Tungsten alloy Powder |
Co21Cr5W0.1C- 1Ni1.5Si2.4B |
-140+325mesh | HRC~50/53, Working temp. <840℃, Great resistance to corrosion & high temperature, a bit self-fluxing. Plasma surfacing for motorcycle valve top. | Inquiry |
| Nickel Chromium Aluminum Yttrium Alloy Powder |
MCrAlY powder Ni22Cr11AlY |
-270+400mesh | HRC~20/30, Working temp. <950℃, Great resistance to corrosion & high temperature, a bit self-fluxing. Plasma surfacing for motorcycle valve top. | Inquiry |
| Cobalt Chromium Aluminum Yttrium Alloy Powder |
MCrAlY powder Co32Ni21Cr8Al0.5Y |
-270+400mesh | HRC~20/30, Working temp. <950℃, Great resistance to heat corrosion, oxidation and vulcanization @ high temperature, used as bonding layer of thermal barrier coatings | Inquiry |
| Cobalt Chromium Tungsten Alloy Powder |
MCrAlY powder CoCrAlYTaSi |
-270+400mesh |
Working temp. <1000℃, used as bonding layer of high temp. coatings, Used to manufacture and repair metallurgical roll, high temperature annealing furnace roll | Inquiry |
| Molybdenum Based Alloy Powder |
Mo30/70Ni60 Mo60/40Ni60 Mo65/35Ni60 Mo70/30Ni60 Mo75/35Ni60 |
-96+45µm -74+38µm -38µm |
Dense & smooth, high bonding strength, excellent resistance to gripping and wear, used as piston ring and synchronizing disc coatings. | Inquiry |
| Iron Based Alloy Powder |
Fe15Cr1B1Si, Fe87Cr13, Fe17Cr12Ni1S- i.4Mn0.1Mn Fe17Cr20Ni4Mo1Mn, Fe13Cr1.6B1.2Si0.8Mo Fe5C1Si1.8B43Cr Fe21Cr1.5B3.5Si10- Ni2Mo0.8Mn0.5V Fe21Cr1.7B3.5Si10- Ni2Mo0.8Mn0.7V Fe6Ni2W13- Cr2.5Mo2.5 Fe5Mn5Si10Ni13Cr, Fe13Mn2Si6Ni13Cr |
-140+325mesh | HRC~25, Working temp. <400-600℃ | Inquiry |
| Aluminum Silicon Alloy Powder | Al12Si | -120+325mesh | Working temp. <340℃, Used to repair Al, Al alloy and Mg alloy parts, Dimension recover and surface complete for casting Al parts. | Inquiry |
| Silver Copper Alloy Powder | Ag18Cu | -120+325mesh | Working temp. <500℃, Good resistance to high temperature sticky, reduce seal wear, also used to braze welding | Inquiry |
Please send your request to sales@edge-techind.com if the material is not listed.