Non-ferrous Metals
Metal Capillary
Advanced Ceramics
Boron Nitride Ceramic
Pyrolytic Boron Nitride
Silicon Nitride Ceramic
Aluminum Nitride Ceramic
Zirconia Ceramic
Alumina Ceramic
Silicon Carbide Ceramic
Deposition Materials
Semimetal Elements
Functional Materials
Neodymium Magnets
Neodymium Disc Magnets
Neodymium Cylinder Magnets
Neodymium Block Magnets
Neodymium Ring Magnets
Neodymium Countersunk Magnets
Magnetic Assemblies
Arc Magnets
Custom Shaped Magnets
Rare Earth Elements
Composites Powder
We provide many kinds of composites powder for thermal spray coating
| Product | Material | Particle size | Application | Inquiry |
| Titanium Carbide Nickel Composite Powder | 99%, TiC-Ni, Customized composition |
15-50μm, etc. |
-Wear-resistant coating | Inquiry |
| Nickel Clad Aluminum Composite Powder | Ni20Al, Ni5Al |
-140/+325 mesh |
-HRC~20, Working temp. <800℃ -Exothermic coated Powder, high bonding strength, oxidation resistant -Manufacture and repair blades of engine and metallurgical fan |
Inquiry |
| Nickel Clad Molybdenum Composite Powder | Ni22MoS2 |
-140/+325 mesh |
-HRC~20, Working temp. <500℃, -Wear reducing material, Good lubricity, Oxyacetylene flame coating -Used for a low friction ring, low friction material, movable seal parts. |
Inquiry |
| Nickel Clad Graphite Powder | Ni25C, Ni50C |
-140/+325 mesh |
-HRC~20, Working temp. <480℃ -Low hardness, good lubricity. -Oxyacetylene flame coating, can be used surface spray for a low friction ring, aircraft compressor Parts, movable seal parts. |
Inquiry |
| Nickel Clad Aluminum Composite Powder | Ni23Al2O3 |
-140/+325 mesh |
-HRC~40, Working temp. <800℃ -High hardness, good wear resistance -Used as bonding layer for Al2O3 spaying |
Inquiry |
| Nickel Clad Tungsten Carbide Powder | WC12Ni |
-140/+325 mesh |
-HRC~62, Working temp. <400℃ High hardness, good wear resistance, wear-resistant coating -Used for thermal power plant fan, flue putter wear coating |
Inquiry |
| Cobalt Clad Tungsten Carbide Powder |
WC12Co WC17Co WC25Co |
-325/+500 mesh |
-HV0.3 800-1300, Working temp. <540℃ -Hard and dense coating with excellent grain wear and abrasive wear resistance -Higher Co content, higher toughness |
Inquiry |
| Cobalt Chrome Clad Tungsten Carbide Powder | WC10Co4Cr |
-325/+500 mesh |
-HV0.3 1000-1300, Working temp. <540℃ -Better corrosion resistance than WC-12Co, but similar were resistance |
Inquiry |
| Nickel Chrome Clad Chromium Carbide Powder | 20NiCr-80Cr3Cr2 |
-325/+500 mesh |
-HV0.3 900-1100, Working temp. <850℃ -Spaying for rower plant boiler tubes, metallurgic-roll, core metallurgic-roll, petroleum shaft. |
Inquiry |
| Nickel Chrome Clad Chromium Carbide Powder | 25NiCr-75Cr3Cr2 |
-325/+500 mesh |
-HV0.3 800-1000, Working temp. <850℃ -Hard & dense coating, ideal coating for wear resistance, oxidization resistance and corrosion resistance at high temperature. |
Inquiry |
| Nickel Chrome Clad Chromium Carbide Powder | 30NiCr-70Cr3Cr2 |
-325/+500 mesh |
-HV0.3 800-1000, Working temp. <850℃, -Lower hardness then Cr3C2-25NiCr, better toughness |
Inquiry |
| Self-bonding Tungsten Carbide Powder |
Al:3.0, Cr:6.0, B:1.0, Si:1.5, C:0.5, Fe:1.5,Co/WC:50.0, Ni: Bal |
-140/+325 mesh |
-HRC-40, Working temp. <550℃, -Excellent coating bonding strength, sued for both working coating and bonging coating |
Inquiry |
| Nickel Chrome Aluminum Powder | NiCr5Al |
-140/+325 mesh |
-HRC-20, Working temp. <800℃, -Excellent bonding coating and oxidization resistance coating at high temperature |
Inquiry |
| NiCoCrAlY Yttria Composite Powder | NiCoCrAlY-Y2O3 |
-140/+325 mesh |
-HRC-20, Working temp. <800℃, -Excellent bonding coating and oxidization resistance coating at high temperature |
Inquiry |
Please send your request to sales@edge-techind.com if the material is not listed.